Appearance
|
White or creamy-white powder
|
|
Moisture Content at 105℃
|
≤3
|
|
Granularity(＞200mesh)
|
≥97%
|
| Gravity（g/cm3） |
1.85
|
|
Bulk Density（g/cm3）
|
≤0.28
|
|
XRD d001（nm）
|
1.3
|
It is specially used for PA polymer and highly polar polymer modification such as PBT, PET.
Original polymerization: Disperse organic montmorillonite powder into the monomer melt or liquid. Make it fully dispersed by high-speed shear or sand milling. Then do the polymerization according to the convention.
Double screw melt extrusion modification: make the organic clay powder and the polymer pellets or powder fully mixed, or add quantitative organic clay powder directly to the inlet of double screw extruder; Control the temperature at each stage and screw speed, get melt extruded. The Amount of organic clay is generally 3-5% of the polymer.
The double screw machine should have a bigger ratio of length / diameter as far as possible and high shear screw structure. The melting temperature should not be too high, to keep the polymer in the extrusion process achieve higher shear strength in order to make montmorillonite layers exfoliated.
Screw extruder should have vacuum exhaust system to timely discharge gases which can be generated in the process of extrusion and guarantee the quality of the squeezed materials.